Effect of postannealing processes on the properties of hot-pressed Bi2Sr2Ca1Cu1.75Na0.25Oy (Bi-2212) ceramics.

Saved in:
Bibliographic Details
Title: Effect of postannealing processes on the properties of hot-pressed Bi2Sr2Ca1Cu1.75Na0.25Oy (Bi-2212) ceramics.
Authors: Özkurt, Berdan1 (AUTHOR) berdanozkurt@tarsus.edu.tr, Madre, M. A.2 (AUTHOR), Sotelo, A.2 (AUTHOR)
Source: Journal of Materials Science: Materials in Electronics. May2023, Vol. 34 Issue 15, p1-9. 9p.
Abstract: In the present work, the effect of different annealing-time on the properties of Bi2Sr2Ca1Cu1.75Na0.25Oy (Bi-2212) superconducting compound is presented. First, the samples were produced by hot-pressing method under 33 MPa pressure at 750 °C in accordance with previous works. After annealing, the samples were kept at 840 °C for 15, 30 and 60 h, respectively, for postannealing process. XRD results demonstrate the formation of Bi-2212 phase in large amount in all samples. SEM images show the formation of different grain morphologies depending on the postannealing time. The sample postannealed for 60 h at 840 °C has the highest superconducting transition temperature (Tc, onset), 91 K, obtained from M–T measurements. The magnetic properties of samples have been investigated using M–H hysteresis loops at 15 K in the range − 1.6 × 106 to + 1.6 106 A/m. The widest M–H curves were obtained in the postannealed sample for 60 h at 840 °C, probably as a result of both the improvement of crystallinity, cleaner grain boundaries and better grain orientation. In addition, the widest hysteresis curve observed in that sample in the entire applied magnetic field range is an indication that it has strong pinning behavior. The critical current density (Jc) was investigated via Bean’s model from these data. Finally, the sample postannealed at 840 °C for 60 h reached a Jc value of 2.903 × 106 A/cm2 at H = 1.9 T and T = 15 K, which is, approximately, 44% higher than the determined in annealed samples (2.015 × 106 A/cm2). [ABSTRACT FROM AUTHOR]
Copyright of Journal of Materials Science: Materials in Electronics is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Full text is not displayed to guests.
FullText Links:
  – Type: pdflink
Text:
  Availability: 1
Header DbId: egs
DbLabel: Engineering Source
An: 163936430
AccessLevel: 6
PubType: Academic Journal
PubTypeId: academicJournal
PreciseRelevancyScore: 0
IllustrationInfo
Items – Name: Title
  Label: Title
  Group: Ti
  Data: Effect of postannealing processes on the properties of hot-pressed Bi<subscript>2</subscript>Sr<subscript>2</subscript>Ca<subscript>1</subscript>Cu<subscript>1.75</subscript>Na<subscript>0.25</subscript>O<subscript>y</subscript> (Bi-2212) ceramics.
– Name: Author
  Label: Authors
  Group: Au
  Data: <searchLink fieldCode="AR" term="%22Özkurt%2C+Berdan%22">Özkurt, Berdan</searchLink><relatesTo>1</relatesTo> (AUTHOR)<i> berdanozkurt@tarsus.edu.tr</i><br /><searchLink fieldCode="AR" term="%22Madre%2C+M%2E+A%2E%22">Madre, M. A.</searchLink><relatesTo>2</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Sotelo%2C+A%2E%22">Sotelo, A.</searchLink><relatesTo>2</relatesTo> (AUTHOR)
– Name: TitleSource
  Label: Source
  Group: Src
  Data: <searchLink fieldCode="JN" term="%22Journal+of+Materials+Science%3A+Materials+in+Electronics%22">Journal of Materials Science: Materials in Electronics</searchLink>. May2023, Vol. 34 Issue 15, p1-9. 9p.
– Name: Abstract
  Label: Abstract
  Group: Ab
  Data: In the present work, the effect of different annealing-time on the properties of Bi2Sr2Ca1Cu1.75Na0.25Oy (Bi-2212) superconducting compound is presented. First, the samples were produced by hot-pressing method under 33 MPa pressure at 750 °C in accordance with previous works. After annealing, the samples were kept at 840 °C for 15, 30 and 60 h, respectively, for postannealing process. XRD results demonstrate the formation of Bi-2212 phase in large amount in all samples. SEM images show the formation of different grain morphologies depending on the postannealing time. The sample postannealed for 60 h at 840 °C has the highest superconducting transition temperature (Tc, onset), 91 K, obtained from M–T measurements. The magnetic properties of samples have been investigated using M–H hysteresis loops at 15 K in the range − 1.6 × 106 to + 1.6 106 A/m. The widest M–H curves were obtained in the postannealed sample for 60 h at 840 °C, probably as a result of both the improvement of crystallinity, cleaner grain boundaries and better grain orientation. In addition, the widest hysteresis curve observed in that sample in the entire applied magnetic field range is an indication that it has strong pinning behavior. The critical current density (Jc) was investigated via Bean’s model from these data. Finally, the sample postannealed at 840 °C for 60 h reached a Jc value of 2.903 × 106 A/cm2 at H = 1.9 T and T = 15 K, which is, approximately, 44% higher than the determined in annealed samples (2.015 × 106 A/cm2). [ABSTRACT FROM AUTHOR]
– Name: AbstractSuppliedCopyright
  Label:
  Group: Ab
  Data: <i>Copyright of Journal of Materials Science: Materials in Electronics is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract.</i> (Copyright applies to all Abstracts.)
PLink https://search.ebscohost.com/login.aspx?direct=true&site=eds-live&db=egs&AN=163936430
RecordInfo BibRecord:
  BibEntity:
    Identifiers:
      – Type: doi
        Value: 10.1007/s10854-023-10650-0
    Languages:
      – Code: eng
        Text: English
    PhysicalDescription:
      Pagination:
        PageCount: 9
        StartPage: 1
    Titles:
      – TitleFull: Effect of postannealing processes on the properties of hot-pressed Bi2Sr2Ca1Cu1.75Na0.25Oy (Bi-2212) ceramics.
        Type: main
  BibRelationships:
    HasContributorRelationships:
      – PersonEntity:
          Name:
            NameFull: Özkurt, Berdan
      – PersonEntity:
          Name:
            NameFull: Madre, M. A.
      – PersonEntity:
          Name:
            NameFull: Sotelo, A.
    IsPartOfRelationships:
      – BibEntity:
          Dates:
            – D: 21
              M: 05
              Text: May2023
              Type: published
              Y: 2023
          Identifiers:
            – Type: issn-print
              Value: 09574522
          Numbering:
            – Type: volume
              Value: 34
            – Type: issue
              Value: 15
          Titles:
            – TitleFull: Journal of Materials Science: Materials in Electronics
              Type: main
ResultId 1